美国标准
( Welded and Seamless ) Properties Minima Unless Stated |
Grade 钢号 |
Chemical Composition 化学成份 % ( Maximum 最大 ) |
Tensile Strength 抗拉强度 |
Yield Stress 屈服强度 |
Elongation 伸长率 on 2 in |
Flattening Test 环装压扁试验 |
Others 其它 |
|||
C |
Mn |
P |
S |
ksi ( N / mm2 ) |
ksi ( N / mm2 ) |
% |
|||
A | 0.26 | - | 0.04 | 0.05 | 45 ( 310 ) | 39 ( 228 ) | 25 |
Weld portion H = 2/3 D The other side of weld H = 1/3 D |
If necessary, stress relieved annealing |
B | 0.26 | - | 0.04 | 0.05 | 58 ( 400 ) | 46 ( 317 ) | 23 | ||
C | 0.23 | 1.35 | 0.04 | 0.05 | 62 ( 427 ) | 50 ( 345 ) | 21 |
欧洲标准
Properties Minima Unless Stated |
Grade 钢号 |
Chemical Composition 化学成份 % ( Maximum 最大 ) |
Tensile Strength 抗拉强度 |
Yield Stress 屈服强度 |
Elongation 伸长率 % No. 5 Test piece |
Impact Strength 冲击功 10 X 10mm specimen |
|||||
C |
Si |
Mn |
P |
S |
N / mm2 |
N / mm2 |
% |
oC |
J | |
S275J0H | 0.20 | - | 1.50 | 0.04 | 0.04 | 410 ~ 560 | 275 | 201) | 0 | 27 |
S275J2H | 0.20 | - | 1.50 | 0.035 | 0.035 | 410 ~ 560 | 275 | 201) | -20 | 27 |
-20 | 27 | |||||||||
S355J2H |
0.22 |
0.55 |
1.60 |
0.035 |
0.035 |
490 ~ 630 |
355 |
201) |
Notes : 1) Elongation at 17% for sizes £ 60mm square or equivalent rectangular or round sections |
日本标准
Properties Minima Unless Stated |
Grade 钢号 |
Chemical Composition 化学成份 % ( Maximum 最大 ) |
Tensile Strength1)2) 屈服强度 |
Yield Stress1)2) 降伏强度 |
Elongation 伸长率 % No. 5 Test piece |
||||
C |
Si |
Mn |
P |
S |
N / mm2 |
N / mm2 |
% |
|
STKR 400 ( STKR 41 ) |
0.25 |
- |
- |
0.04 |
0.04 |
400 |
245 |
23 |
STKR 490 ( STKR 50 ) |
0.18 |
0.55 |
1.50 |
0.04 |
0.04 |
490 |
325 |
23 |
Notes : 1) When the tube under 8mm in thickness is subjected to tensile test, the minimum value of elongation shall be calculated by subtracting 1.5% from the value of elongation given in above table or each decrease of 1mm and rounding off the result to a whole number according to JIS Z8401 2) When a tensile test piece is to be taken from the welded steel square tube, one shall be taken form a seamless portion. |
日本标准
Properties Minima
Unless Stated
Designation 钢号 |
Chemical Composition 化学成份 % ( Maximum 最大 ) |
Tensile Strength2) 抗拉强度 |
Elongation2) 伸长率% (min.最小) |
Test Piece 测试片
|
Bending Test2) 弯曲试验 |
||||||||||
C |
Si |
Mn |
P |
S |
N / mm |
thickness 厚度 ( mm ) |
Bending Angle 弯曲角度 |
Inside Radius 半径内 |
Test Piece 测试片 |
||||||
Thickness 厚度 t ( mm ) |
|||||||||||||||
1.2£t<1.6 | 1.6£t<3.0 | 3.0£t<6.0 | 6.0£t<13.0 | ||||||||||||
t£3.0 |
3.0<t£13.0 | ||||||||||||||
SPHT 1 | 0.10 | 0.351) | 0.5 | 0.04 | 0.04 | 270 | 30 | 32 | 35 | 37 | No. 5 rolling direction | 180o | Flat on itself | 0.5 t | No. 3 rolling direction |
SPHT 2 | 0.18 | 0.35 | 0.6 | 0.04 | 0.04 | 340 | 25 | 27 | 30 | 32 | 180o | 1.0 t | 1.5 t | ||
SPHT 3 | 0.25 | 0.35 | 0.30 ~ 0.90 | 0.04 | 0.04 | 410 | 20 | 22 | 25 | 27 | 180o | 1.5 t | 2.0 t | ||
SPHT 4 | 0.30 | 0.35 | 0.30 ~ 1.00 | 0.04 | 0.04 | 490 | 15 | 18 | 20 | 22 | 180o | 1.5 t | 2.0 t |
Notes : 1) When agreed upon between the concerned parties, Si content may be modified to 0.04% max. 2) Mechanical test values are not applicable to the irregular portions at either end of the steel strip. |
英国标准
Grade5) 钢号 |
BS
4360
Equivalent |
Type
of
Oxidation3) 氧化方法 |
Chemical Composition 化学成份 % |
Mechanical Properties 机械性能 (Minimum最小) |
||||||||||||||
C |
Si |
Mn |
P |
S |
N1)2) |
Yield Stress2) N/mm2 屈服强度 |
Tensile Strength N/mm2 抗拉强度 |
Elongation3)4) 伸长率 % |
Impact Test 冲击功 J for t£65 Average 3 tests |
|||||||||
Thickness 厚度 t mm |
Thickness 厚度 t mm |
Thickness 厚度 t mm |
Thickness 厚度 t mm |
|||||||||||||||
t£40 |
40<t£65 |
t£16 |
16<t£40 |
40<t£65 |
t£3 |
3<t £65 |
t£40 |
40<t £65 |
||||||||||
maximum 最大 |
0oC | -20oC | ||||||||||||||||
S275J0H | 43C | FN | 0.20 | 0.22 | - | 1.50 | 0.040 | 0.040 | 0.009 | 275 | 265 | 255 | 430/580 | 410/560 | 22 (20) | 21 (19) | 27 | - |
S275J2H | 43D | FF | 0.20 | 0.22 | - | 1.50 | 0.035 | 0.035 | - | 275 | 265 | 255 | 430/580 | 410/560 | 22 (20) | 21 (19) | - | 27 |
S355J0H | 50C | FN | 0.22 | 0.22 | 0.55 | 1.60 | 0.040 | 0.040 | 0.009 | 355 | 345 | 335 | 510/680 | 490/630 | 22 (20) | 21 (19) | 27 | - |
S355J2H | 50D | FF | 0.22 | 0.22 | 0.55 | 1.60 | 0.035 | 0.035 | - | 355 | 345 | 335 | 510/680 | 490/630 | 22 (20) | 21 (19) | - | 27 |
Notes:
1) It is permissible to exceed the specified values provided that for each increase of 0.001% N, the P max. content will be reduced by 0.005%, the ladle N content however shall be 0.012% max. 2) The max. value for N does not apply if min. 0.02% of Al present 3) FN = rimming steel not permitted, FF = fully killed steel containing N binding elements, GL = 5.65ÖSo 4) Values in brackets are transverse direction properties |